| Product Information | Ultramid® B3WG6 BGVW BK00564 | |||||||
| 04/2025 | PA6-GF30 | |||||||
| Product Information | ||||||||
| Glass fibre reinforced and heat ageing resistant injection moulding grade used e.g. for automobile manifolds | ||||||||
| Physical form and storage | ||||||||
| The product is supplied in the form of granules with a bulk density of approx. 0.7 g/cm³ . Standard packs are bag and bulk container (octagonal IBC=intermediate bulk container made from corrugated board with a liner bag). Other packaging materials and shipping in road or rail silo wagons are possible by agreement. The containers should only be opened immediately before processing or drying. To ensure that the delivered product absorbs as little moisture as possible, the containers should be stored in dry rooms and always carefully closed again after partial quantities have been withdrawn.In principle, the product can be stored for a long period of time. Containers stored in cold rooms should be equalized to ambient temperature before opening in order to avoid condensation on the granules. Regardless of the storage conditions,the product should be pre-dried according to our recommendations and the machine should preferably be loaded using a closed conveyor system. | ||||||||
| Product safety | ||||||||
| In case processing is done under conditions as recommended (cf. processing data sheet) melts are thermally stable and do not generate hazards by molecular degradation or the evolution of gases and vapors. Like all thermoplastic polymers the product decomposes on exposure to excessive thermal load, e.g. when it is overheated or as a result of cleaning by burning off. Further information is available from the safety data sheet. | ||||||||
| Note | ||||||||
| The data contained in this publication are based on our current knowledge and experience. In view of the many factors that may affect processing and application of our product, these data do not relieve processors from carrying out their own investigations and tests; neither do these data imply any guarantee of certain properties, nor the suitability of the product for a specific purpose. Any descriptions, drawings, photographs, data, proportions, weights etc. given herein may change without prior information and do not constitute the agreed contractual quality of the product. It is the responsibility of the recipient of our products to ensure that any proprietary rights and existing laws and legislation are observed.In order to check the availability of products please contact us or our sales agency. | ||||||||
| BASF SE | ||||||||
| 67056 Ludwigshafen, Germany |
| Ultramid® B3WG6 BGVW BK00564 | ||||||||
| Product Information | ||||||||
| Typical values for uncoloured product at 23 °C 1) | Test method | Unit | Values 2) | |||||
| Properties（基础物性） | ||||||||
| Polymer abbreviation | – | – | PA6-GF30 | |||||
| Density | ISO 1183 | kg/m³ | 1360 | |||||
| Viscosity number (0.5% in 96% H2SO4 ) | ISO 307, 1157, 1628 | cm³/g | 142 | |||||
| Water absorption, saturation in water at 23°C | similar to ISO 62 | % | 6.3 – 6.9 | |||||
| Moisture absorption, equilibrium 23°C/50% r.h. | similar to ISO 62 | % | 1.9 – 2.3 | |||||
| Processing（加工参数） | ||||||||
| Melting temperature, DSC | ISO 11357-1/-3 | °C | 220 | |||||
| Melt temperature, injection moulding/extrusion | – | °C | 270 – 290 | |||||
| Mould temperature, injection moulding | – | °C | 80 – 90 | |||||
| Moulding shrinkage, constrained 3) | – | % | 0.25 | |||||
| Pre/Post-processing, Pre-drying, Temperature– | – | °C | 80 | |||||
| Pre/Post-processing, Pre-drying, Time | – | h | 4 | |||||
| Flammability（阻燃性） | ||||||||
| UL94 flammability rating at nominal 1.5 mm (thickness tested) | IEC 60695-11-10 | class (mm) | HB (-) | |||||
| Automotive materials (Thickness >= 1 mm)4) | ISO 3795, FMVSS 302 | – | + | |||||
| Mechanical properties （机械物性） | dry / cond. | |||||||
| Tensile modulus | ISO 527-1/-2 | MPa | 9600 / 5600 | |||||
| Stress at break | ISO 527-1/-2 | MPa | 180 / 90 | |||||
| Strain at break | ISO 527-1/-2 | % | 3 / 6 | |||||
| Flexural modulus | ISO 178 | MPa | 8300 / 5000 | |||||
| Flexural strength | ISO 178 | MPa | 250 / 150 | |||||
| Charpy unnotched impact strength (23°C) | ISO 179/1eU | kJ/m² | 80 / 80 | |||||
| Charpy unnotched impact strength (-30°C) | ISO 179/1eU | kJ/m² | 65 / – | |||||
| Charpy notched impact strength (23°C) | ISO 179/1eA | kJ/m² | 46011 | |||||
| Charpy notched impact strength (-30°C) | ISO 179/1eA | kJ/m² | 9 / – | |||||
| Izod notched impact strength (23°C) | ISO 180/A | kJ/m² | 12 / – | |||||
| Thermal properties | ||||||||
| Deflection temp. under load 1.8 MPa (HDTA) Deflection temp. under load 0.45 MPa (HDT B) Max. service temperature (short cycle operation) | ISO 75-1/-2 ISO 75-1/-2 | °C °C °C | 205 218 200 | |||||
| Coefficient of linear thermal expansion, longitudinal (23-55)°C Coefficient of linear thermal expansion, transverse (23-55)°C | ISO 11359-1/-2 ISO 11359-1/-2 | E-6/K E-6/K | 18.4 96.4 | |||||
| Electrical properties | ||||||||
| Electric strength K20/K20, (60*60*1 mm³) | IEC 60243-1 | kV/mm | 40 / 31 | |||||
Footnotes
1) If product name or properties don’t state otherwise.
2) The asterisk symbol ‘*’ signifies inapplicable properties.
3) Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 280°C, TW = 80°C
4) + = passed
（免责声明：资料来源于网络，仅供学习交流，如有疑问，请联系生产厂家，以厂家说法为准，本资料版权归属于原作者，如有侵权，请联系删除）
可提供的报告：
TDS(ISO标准物性表)、SDS(安全物质表)、REACH、RoHS（环保报告）、UL（黄卡）、SVHC
Email:info@plaspowers.com
www.plaspowers.com
sister corporation:Sunengtag
Wechat: sunengpv
评价
目前还没有评价