伊士曼 Tritan PCTG TX1001 基本物性参数
Typical Properties
| Propertya | Test Methodb | Typical Value, Unitsc | |
| General Properties | |||
| Specific Gravity | D 792 | 1.18 | |
| Mold Shrinkage | D 955 | 0.005-0.007 mm/mm (0.005-0.007 in./in.) | |
| Mechanical Properties (ISO Method) | |||
| Tensile Stress @ Yield | ISO 527 | 43 MPa | |
| Tensile Strength @ Break | ISO 527 | 58 MPa | |
| Elongation @ Yield | ISO 527 | 7 % | |
| Elongation @ Break | ISO 527 | 185 % | |
| Tensile Modulus | ISO 527 | 1548 MPa | |
| Flexural Modulus | ISO 178 | 1495 MPa | |
| Flexural Strength | ISO 178 | 59 MPa | |
| Izod Impact Strength, Notched | |||
| @ 23°C | ISO 180 | 93 kJ/m2 | |
| @ -40°C | ISO 180 | 20 kJ/m2 | |
| Mechanical Properties | |||
| Tensile Stress @ Yield | D 638 | 43 MPa (6200 psi) | |
| Tensile Stress @ Break | D 638 | 53 MPa (7700 psi) | |
| Elongation @ Yield | D 638 | 6 % | |
| Elongation @ Break | D 638 | 210 % | |
| Tensile Modulus | D 638 | 1550 MPa (2.25 x 105 psi) | |
| Flexural Modulus | D 790 | 1550 MPa (2.25 x 105 psi) | |
| Flexural Yield Strength | D 790 | 62 MPa (9000 psi) | |
| Rockwell Hardness, R Scale | D 785 | 112 | |
| Izod Impact Strength, Notched | |||
| @ 23°C (73°F) | D 256 | 980 J/m (18.4 ft·lbf/in.) | |
| Impact Strength, Unnotched | |||
| @ 23°C (73°F) | D 4812 | NB | |
| Optical Properties | |||
| Total Transmittance | D 1003 | 90 % | |
| Haze | D 1003 | <1 % | |
| Thermal Properties | |||
| Deflection Temperature | |||
| @ 0.455 MPa (66 psi) | D 648 | 99 °C (210 °F) | |
| @ 1.82 MPa (264 psi) | D 648 | 85 °C (185 °F) | |
| Typical Processing Conditions | |||
| Drying Temperature | 88 °C (190 °F) | ||
| Drying Time | 4-6 hrs | ||
| Processing Melt Temperature | 260-282 °C (500-540 °F) | ||
| Mold Temperature | 38-66 °C (100-150 °F) | ||
aUnless noted otherwise, all tests are run at 23°C (73°F) and 50% relative humidity.
bUnless noted otherwise, the test method is ASTM.
cUnits are in SI or US customary units.
Technical Disclaimer
Eastman makes no representation and disclaims any warranty that the material in any particular shipment will conform exactly to the values given. Values as well as the performance of the final molded article may be affected by various factors such as the part design, mold design or tooling, drying, processing conditions as well as coloring or pigmentation of the product. No warranty of merchantability or fitness for use is made, and nothing herein waives any of the Seller””””””””s conditions of sale. You must make your own determination of the suitability of this product in your specific application due to the many factors (e.g. design, processing and conditions of use) that affect the performance of the final molded article. Suitability of use should be evaluated with appropriate testing and analysis. The processing melt temperature and mold temperature refer to the actual resin melt temperature and actual mold surface temperature respectively. Consider overall resin residence time, part shot size utilization and part geometry to set appropriate processing melt temperature and mold temperature in order to minimize IV loss and maximize molded part performance.
Comments
Properties reported here are based on limited testing. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given.
Eastman and its marketing affiliates shall not be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller’s conditions of sale.
| 8/21/2024 9:07:18 AM |