埃克森美孚（ExxonMobil）™ HDPE HD6480
(曾用名： ExxonMobiTM HDPE HMA 025)
物性表（TECHNICAL DATASHEET）
| HMA025 是一种高密度聚乙烯牌号，其特点为具有卓越的外形稳定性、冲击强度和极高的挺度。 | |||||
| 总体 | |||||
| 供货地区1 | .非洲和中东 | .欧洲 | .亚太地区 | ||
| 添加剂 | · 热稳定剂：是 | ·紫外稳定剂：否 | |||
| 应用 | · 工业用桶 ·蔬菜和瓶装品板条箱 | ||||
| 修订信息 ·01/01/2017 | |||||
| 物理性能 | 典型数值 | (英制) | 典型数值 | (公制) | 测试方法 |
| 密度 | 0.964 | g/cm³ | 0.964 | g/cm³ | ASTM D1505 |
| 熔融指数(190°C/2.16kg) | 8.0 | g/10 mn | 8.0 | g/10 min | ASTMD1238 |
| 热性能 | 典型数值 | (英制) | 典型数值 | (公制) | 测试方法 |
| 热变形温度B法(0.45MPa)未退火 | 150 | F | 66 | C | ISO 75-2/B |
| 熔融峰值温度 | 275 | ‘F | 135 | C | ASTM D3418 |
| 被铸造的物产 | 典型数值 | (英制) | 典型数值 | (公制) | 测试方法 |
| 拉伸屈服应力 | 3900 | psi | 27 | MPa | ISO 527-2/1A/50 |
| 拉伸屈服应变 | 9 | % | 9 | % | ISO 527-2/1A/50 |
| 拉伸断裂应变 | >100 | % | >100 | % | ISO 527-2/1A/50 |
| 弯曲模量 | 170000 | psi | 1200 | MPa | ISO 178 |
| 抗环境应力开裂(122*F(50°C),10% Igepal) | 4 | hr | 4 | hr | ASTM D1693 |
| 冲击性能 | 典型数值 | (英制) | 典型数值 | (公制) | 测试方法 |
| 悬壁梁缺口冲击强度 | 2.8 | ft ·Ib/in² | 6.0 | kJ/m² | ISO 180/1A |
| Product Description | ||||||
| ExxonMobil™ HD6480 is a HDPE grade,characterized by excellent dimensional stability,impact strength and very high stiffness. | ||||||
| General | ||||||
| Availability1 | ·Africa &Middle East | ·Asia Pacific | ·Europe | |||
| Additive | ·Thermal Stabilizer:Yes | ·UV Stabilizer:No | ||||
| Applications | ·Industrial Pails | ·Vegetable and Bottle Crates | ||||
| Revision Date | ·01/01/2017 | |||||
| Resin Properties | Typical Value (English) | Typical Value (SI) | Test Based On | |||
| Density | 0.964 g/cm³ | 0.964 g/cm³ | ASTM D1505 | |||
| Melt Index(190°C/2.16kg) | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 | |||
| Thermal | Typical Value (English) | Typical Value (SI) | Test Based On | |||
| Heat Deflection Temperature(0.45 MPa) | 150 °F | 66 ℃ | ISO75-2/B | |||
| Peak Melting Temperature | 275 °F | 135 ℃ | ASTM D3418 | |||
| Molded Properties | Typical Value (English) | Typical Value (SI) | Test Based On | |||
| Tensile Stress at Yield | 3900 psi | 27 MPa | ISO 527-2/1A/50 | |||
| Tensile Strain at Yield | 9 % | 9 % | ISO 527-2/1A/50 | |||
| Tensile Strain at Break | >100 % | >100 % | ISO 527-2/1A/50 | |||
| Flexural Modulus | 170000 psi | 1200 MPa | ISO 178 | |||
| Environmental Stress-Crack Resistance 122°F(50℃),10%Igepal | ASTM D1693 | |||||
| 4 hr | 4 hr | |||||
| Impact Typical Value(English) Typical Value(SI) Test Based On | ||||||
| Notched lzod Impact Strength 2.8 ft·lb/in² 6.0 kJ/m² ISO 180/1A |
| Additional Information | ||||||
| The molded properties were measured on 4mm(157.5mil)thick injection molded specimen based on ISO 294-1. Heat Deflection temperature sample preparation,injection based on ISO1872.Tested flat wise position with specimen size of 80mm×10mmx4mm. ESCR was measured on 2mm(78.7 mil)thick compression molded plate(F50,10%Igepal,50℃,122°F) |
| Legal Statement | ||||||
| Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance(eg.FDA,EU,HPFB). This product is not intended for use in medical applications and should not be used in any such applications. |
| Notes | ||||||
| Typical properties:these are not to be construed as specifications. 1 Product may not be available in one or more countries in the identified Availability regions.Please contact your Sales Representative for complete Country Availability. |
（以上信息来自于网络资料，对其中数据如有疑问，请咨询原厂，以原厂说法为准，资料版权归属于原作者，仅善意用于同行间学习交流，如有侵权，请联系删除）