PC LUPOY 1201是韩国LG化学生产的一款食品级通用聚碳酸酯（PC），按熔指分为三个产品型号，1201-10p,1201-15,1201-22,其中的后缀代表的是熔指。

PC LUPOY 1201 designed for FDA related or general injection molding with high impact strength and transparency.

特点：食品级、易加工。

Key Features:FDA, Good Mold Release.

应用：电子烟、水杯、展柜、中大件产品。

Applications：Compound, Food Packaging, Vacuum Cleaner, E&E Others, Sundry Goods

订购电话：0769-87126376  17688193619

获取报价：联系塑能

分类： 标签： , , ,

LG 化学（LG Chem）

食品级 PC  LUPOY ™️1201

物性表（TECHNICAL  DATASHEET）

 PC 1201-10P物性表：

 PC 1201-10P
 PC 1201-10P Description
It is designed for FDA related or general injection molding with high impact strength and transparency.
ApplicationKey Features
Sheet/Flim, Vacuum Cleaner, E&E OthersFDA, Good Mold Release, High Impact Resistance, High Transparency
PropertiesMethodUnitPC 1201-10P
Physical
Melt Flow Rate (300 °C /1.2 kg)ASTM D1238g/10min10
DensityASTM D792kg/m³1200
Mold ShrinkageASTM D955㎜/㎜0.005~0.007
Water Absorption @ 24 hrs, 23°CASTM D570%0.15
Water Absorption @ equilibrium, 50%RH, 23°CASTM D570%0.32
Optical
Refractive Index, nDASTM D5421.586
Light TransmittanceASTM D1003%89
HazeASTM D1003%0.7~1.5
Thermal
Deflection Temperature Under Load (DTUL) @ 4 mm 66
psi (0.45 MPa), annealed		ASTM D648℃144
Deflection Temperature Under Load (DTUL) @ 4 mm
264 psi (1.8 MPa), annealed		ASTM D648℃141
Deflection Temperature Under Load (DTUL) @ 4 mm
264 psi (1.8 MPa), unannealed		ASTM D648℃128
Vicat Softening Point, 50°C /hr, 50N LoadASTM D1525℃149
Coefficient of Linear Thermal Expansion, @ -40 to 82°CASTM D696mm/mm/℃68 x 10^-6
Mechanical
Tensile Yield StrengthASTM D638MPa60
Ultimate Tensile StrengthASTM D638MPa71
Elongation at YieldASTM D638%6
Elongation at BreakASTM D638%150
Tensile ModulusASTM D638MPa2410
Flexural StrengthASTM D790MPa96
Flexural ModulusASTM D790MPa2410
Notched Izod Impact @ 23 °CASTM D256J/m900
Unnotched Izod Impact @ 23 °CASTM D256No break
Instrumented Dart Impact, Total Energy @ 23 °CASTM D3763J87
Rockwell Hardness @ R ScaleASTM D785R Scale118
Rockwell Hardness @ M ScaleASTM D785M Scale73
Taber Abrasion Resistance (D Haze)ASTM D1044%45
Ignition Resistance
UL-94 @ 0.5 mmASTM D635V-2
UL-94 @ 1.6 mmASTM D635V-2
UL-94 @ 2.5-2.7 mmASTM D635V-2
UL-94 @ 3.0 mmASTM D635HB
Limiting Oxygen IndexASTM D2863%26
Ball Indentation TemperatureIEC 598-1℃>125
Average Extent of BurningASTM D635mm25
Electrical
GWT 2.0 mm, 5 secondIEC 695-2-1℃850
Comparative Tracking Index @ 2.0 mmIEC 112V250
Dielectric StrengthASTM D149KV/mm17
Dielectric Constant @ 60 HzASTM D1503
Dissipation Factor @ 60 HzASTM D1500.001
Volume Resistivity @ 23 °C, dryASTM D257W-cm2.0 x 10^17
Note
1. When used unmodified for the manufacture of food contact articles LUPOY 1201-10 Polycarbonate resins comply with the U.S. Food, Drug, and CosmeticAct and Food Additive Regulations 21CFR 177.1580 and E.U. Food Contact Regulations. The uses cited above are subject to GMP (Good Manufacturing Practices) and any limitations that are part of the regulations.

The regulations should be consulted for complete details.
2. Typical properties; not to be constructed as specifications.
3. Tensile Test @ 23 °C; 50 mm/min.
4. 0.125 in; 10 mil notch (3.2 mm; 0.25 mm notch).
5. 0.125 in; 8000 ipm (3.2 mm; 203 m/min).
6. 1,000 g; CS-10 F wheel; 500 cycles.
7. These numerical flame spread ratings are small-scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions. UL 94 file: E67171.

※ Typical values are only for material selection purpose, and variation within normal tolerances are for various colors.

Values given should not be interpreted as specification and not be used for part or tool design.

All properties, except melt flow rate are measured on injection molded specimens and after 48 hours storage at 23℃, 50% relative humidity.

Issued Date : 2022-02-16

 PC 1201-15物性表：

 PC 1201-15
PC 1201-15 Description
It is designed for FDA related or general injection molding with high flowability and transparency.
ApplicationKey Features
Compound, Food Packaging, Vacuum Cleaner, E&E Others,Sundry Goods   FDA, Good Mold Release, High Flow, High Transparency
PropertiesMethodUnitPC 1201-15
Physical
Melt Flow Rate (300 °C /1.2 kg)ASTM D1238g/10min15
DensityASTM D792kg/m³1200
Mold ShrinkageASTM D955㎜/㎜0.005~0.007
Water Absorption @ 24 hrs, 23°CASTM D570%0.15
Water Absorption @ equilibrium, 50%RH, 23°CASTM D570%0.32
Optical
Refractive Index, nDASTM D5421.586
Light TransmittanceASTM D1003%89
HazeASTM D1003%0.7~1.5
Thermal
Deflection Temperature Under Load (DTUL) @ 4 mm 66
psi (0.45 MPa), annealed		ASTM D648℃143
Deflection Temperature Under Load (DTUL) @ 4 mm
264 psi (1.8 MPa), annealed		ASTM D648℃140
Deflection Temperature Under Load (DTUL) @ 4 mm
264 psi (1.8 MPa), unannealed		ASTM D648℃127
Vicat Softening Point, 50°C /hr, 50N LoadASTM D1525℃148
Coefficient of Linear Thermal Expansion, @ -40 to 82°CASTM D696mm/mm/℃68 x 10^-6
Mechanical
Tensile Yield StrengthASTM D638MPa60
Ultimate Tensile StrengthASTM D638MPa71
Elongation at YieldASTM D638%6
Elongation at BreakASTM D638%150
Tensile ModulusASTM D638MPa2340
Flexural StrengthASTM D790MPa96
Flexural ModulusASTM D790MPa2410
Notched Izod Impact @ 23 °CASTM D256J/m850
Unnotched Izod Impact @ 23 °CASTM D256No break
Instrumented Dart Impact, Total Energy @ 23 °CASTM D3763J87
Rockwell Hardness @ R ScaleASTM D785R Scale118
Rockwell Hardness @ M ScaleASTM D785M Scale72
Taber Abrasion Resistance (D Haze)ASTM D1044%45
Ignition Resistance
UL-94 @ 0.5 mmASTM D635V-2
UL-94 @ 1.6 mmASTM D635V-2
UL-94 @ 2.5-2.7 mmASTM D635V-2
UL-94 @ 3.0 mmASTM D635HB
Limiting Oxygen IndexASTM D2863%26
Ball Indentation TemperatureIEC 598-1℃>125
Average Extent of BurningASTM D635mm25
Electrical
GWT 2.0 mm, 5 secondIEC 695-2-1℃850
Comparative Tracking Index @ 2.0 mmIEC 112V250
Dielectric StrengthASTM D149KV/mm17
Dielectric Constant @ 60 HzASTM D1503
Dissipation Factor @ 60 HzASTM D1500.001
Volume Resistivity @ 23 °C, dryASTM D257W-cm2.0 x 10^17
Note
1. When used unmodified for the manufacture of food contact articles LUPOY 1201-15 Polycarbonate resins comply with the U.S. Food, Drug, and Cosmetic Act and Food Additive Regulations 21 CFR 177.1580 and E.U. Food Contact Regulations. The uses cited above are subject to GMP (Good Manufacturing Practices) and any limitations that are part of the regulations.The regulations should be consulted for complete details.
2. Typical properties; not to be constructed as specifications.
3. Tensile Test @ 23 °C; 50 mm/min.
4. 0.125 in; 10 mil notch (3.2 mm; 0.25 mm notch).
5. 0.125 in; 8000 ipm (3.2 mm; 203 m/min).
6. 1,000 g; CS-10 F wheel; 500 cycles.
7. These numerical flame spread ratings are small-scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions. UL 94 file: E67171.※ Typical values are only for material selection purpose, and variation within normal tolerances are for various colors.
Values given should not be interpreted as specification and not be used for part or tool design.
All properties, except melt flow rate are measured on injection molded specimens and after 48 hours storage at 23℃, 50% relative humidity.

Issued Date : 2022-02-16

PC 1201-22物性表：

 PC 1201-22
 PC 1201-22 Description
It is designed for FDA related or general injection molding with high flowability and transparency.
ApplicationKey Features
Compound, Food Packaging, Vacuum Cleaner, E&E Others, Sundry GoodsFDA, Good Mold Release, High Flow, High Transparency
PropertiesMethodUnitPC 1201-22
Physical
Melt Flow Rate (300 °C /1.2 kg)ASTM D1238g/10min22
DensityASTM D792kg/m³1200
Mold ShrinkageASTM D955㎜/㎜0.005~0.007
Water Absorption @ 24 hrs, 23°CASTM D570%0.15
Water Absorption @ equilibrium, 50%RH, 23°CASTM D570%0.32
Optical
Refractive Index, nDASTM D5421.586
Light TransmittanceASTM D1003%89
HazeASTM D1003%0.7~1.5
Thermal
Deflection Temperature Under Load (DTUL) @ 4 mm 66
psi (0.45 MPa), annealed		ASTM D648℃142
Deflection Temperature Under Load (DTUL) @ 4 mm
264 psi (1.8 MPa), annealed		ASTM D648℃139
Deflection Temperature Under Load (DTUL) @ 4 mm
264 psi (1.8 MPa), unannealed		ASTM D648℃126
Vicat Softening Point, 50°C /hr, 50N LoadASTM D1525℃147
Coefficient of Linear Thermal Expansion, @ -40 to 82°CASTM D696mm/mm/℃68 x 10^-6
Mechanical
Tensile Yield StrengthASTM D638MPa60
Ultimate Tensile StrengthASTM D638MPa66
Elongation at YieldASTM D638%6
Elongation at BreakASTM D638%120
Tensile ModulusASTM D638MPa2340
Flexural StrengthASTM D790MPa96
Flexural ModulusASTM D790MPa2410
Notched Izod Impact @ 23 °CASTM D256J/m750
Unnotched Izod Impact @ 23 °CASTM D256No break
Instrumented Dart Impact, Total Energy @ 23 °CASTM D3763J72
Rockwell Hardness @ R ScaleASTM D785R Scale118
Rockwell Hardness @ M ScaleASTM D785M Scale72
Taber Abrasion Resistance (D Haze)ASTM D1044%45
Ignition Resistance
UL-94 @ 0.5 mmASTM D635V-2
UL-94 @ 1.6 mmASTM D635V-2
UL-94 @ 2.5 mmASTM D635V-2
UL-94 @ 3.0 mmASTM D635V-2
Limiting Oxygen IndexASTM D2863%26
Ball Indentation TemperatureIEC 598-1℃>125
Average Extent of BurningASTM D635mm25
Electrical
GWT 2.0 mm, 5 secondIEC 695-2-1℃850
Comparative Tracking Index @ 2.0 mmIEC 112V250
Dielectric StrengthASTM D149KV/mm17
Dielectric Constant @ 60 HzASTM D1503
Dissipation Factor @ 60 HzASTM D1500.001
Volume Resistivity @ 23 °C, dryASTM D257W-cm2.0 x 10^17
Note
1. When used unmodified for the manufacture of food contact articles LUPOY 1201-22 Polycarbonate resins comply with the U.S. Food, Drug, and Cosmetic Act and Food Additive Regulations 21
CFR 177.1580 and E.U. Food Contact Regulations. The uses cited above are subject to GMP (Good Manufacturing Practices) and any limitations that are part of the regulations.The regulations
should be consulted for complete details.
2. Typical properties; not to be constructed as specifications.
3. Tensile Test @ 23 °C; 50 mm/min.
4. 0.125 in; 10 mil notch (3.2 mm; 0.25 mm notch).
5. 0.125 in; 8000 ipm (3.2 mm; 203 m/min).
6. 1,000 g; CS-10 F wheel; 500 cycles.
7. These numerical flame spread ratings are small-scale test values and are not intended to reflect hazards presented by these or any other materials under actual fire conditions. UL 94 file: E67171.※ Typical values are only for material selection purpose, and variation within normal tolerances are for various colors.
Values given should not be interpreted as specification and not be used for part or tool design.
All properties, except melt flow rate are measured on injection molded specimens and after 48 hours storage at 23℃, 50% relative humidity.

Issued Date : 2022-02-16

（免责声明：资料来源于网络，仅供学习交流，如有疑问，请联系生产厂家，以厂家说法为准，本资料版权归属于原作者，如有侵权，请联系删除）

提供的资料：

物性参数表（TDS-IOS）、COA（出厂物性检测表）、UL（黄卡）、MSDS（安全物质表）、ROHS（环保报告，SGS检测提供）、加工建议参数表

查看更多PC

Email:info@plaspowers.com 
www.plaspowers.com
sister corporation:Sunengtag
Wechat: sunengpv

wechat_orcode

评价

目前还没有评价

成为第一个“1201” 的评价者

您的邮箱地址不会被公开。 必填项已用 * 标注

相关产品

您不能复制此页面的内容