杜邦（Dupont）™ derin®
POM 100P
物性表（TECHNICAL DATASHEET）
| Delrine 100P is a high viscosity acetal homopolymer for use in easy-to-fill molds.Delrino 100P provides a great combination of toughness | |||
| and strength,improved processing thermal stability and productivity for injection molding,andlow VOC emissions. | |||
| 100P General information | Value | Unit | Test Standard |
| Resin Identification | POM | – | ISO 1043 |
| Part Marking Code | POM | – | ISO 11469 |
| Rheological properties | Value | Unit | Test Standard |
| Melt volume-flow rate | 2.2 | cm³/10mi n | ISO 1133 |
| Temperature | 190 | ℃ | ISO 1133 |
| Load | 2.16 | kg | ISO 1133 |
| Melt mass-flow rate | 2.6 | g/10min | ISO 1133 |
| Molding shrinkage,parallel | 2.2 | % | ISO 294-4,2577 |
| Molding shrinkage,normal | 1.9 | % | ISO 294-4,2577 |
| Mechanical properties | Value | Unit | Test Standard |
| Tensile Modulus | 2950 | MPa | SO 527-1/-2 |
| Yield stress | 71 | MPa | SO 527-1/-2 |
| Yield strain | 25 | % | ISO 527-1/-2 |
| Nominal strain at break | 45 | % | ISO 527-1/-2 |
| Flexural Modulus | 2850 | MPa | ISO 178 |
| Flexural Stress at 3.5% | 77 | MPa | ISO 178 |
| Poisson’s ratio | 0.35 | ISO 527-1/-2 | |
| Tensile creep modulus | ISO 899-1 | ||
| 1h | 2700 | MPa | |
| 1000h | 1500 | MPa | |
| Charpy impact strength | ISO 179/1eU | ||
| 73°F | N | kJ/m² | |
| -22°F | 400 | kJ/m² | |
| Charpy notched impact strength | SO 179/1eA | ||
| 73°F | 15 | kJ/m² | |
| -22°F | 14 | kJ/m² | |
| lzod notched impact strength | ISO 180/1A | ||
| 73°F | 14 | kJ/m² | |
| -40°F | 12 | kJ/m² | |
| Hardness,Rockwell,M-scale | 88 | SO 2039-2 | |
| Hardness,Rockwell,R-scale | 119 | SO 2039-2 | |
| Thermal properties | Value | Unit | Test Standard |
| Melting temperature,18°F/min | 178 | ℃ | ISO 11357-1/-3 |
| Temp.of deflection under load | ISO 75-1/-2 | ||
| 260 psi | 95 | ℃ | |
| 65 psi | 155 | ℃ | |
| Vicat softening temperature | ISO 306 | ||
| 90°F/h,11 lbf | 160 | ℃ | |
| 90°F,2 lbf | 175 | ℃ | |
| Coeff.of linear therm.expansion,parallel | 110 | E-6/K | SO 11359-1/-2 |
| Coeff.of linear therm.expansion | ISO 11359-1/-2 | ||
| normal | 110 | E-6/K | |
| Normal,-40-23°℃ | 100 | E-6/K | |
| Parallel,-40-23°℃ | 100 | E-6/K | |
| 100P General information | Value | Unit | Test Standard |
| Resin Identification | POM | – | ISO 1043 |
| Part Marking Code | POM | – | ISO 11469 |
| Rheological properties | Value | Unit | Test Standard |
| Melt volume-flow rate | 2.2 | cm³/10mi n | ISO 1133 |
| Temperature | 190 | ℃ | ISO 1133 |
| Load | 2.16 | kg | ISO 1133 |
| Melt mass-flow rate | 2.6 | g/10min | ISO 1133 |
| Molding shrinkage,parallel | 2.2 | % | ISO 294-4,2577 |
| Molding shrinkage,normal | 1.9 | % | ISO 294-4,2577 |
| Mechanical properties | Value | Unit | Test Standard |
| Tensile Modulus | 2950 | MPa | SO 527-1/-2 |
| Yield stress | 71 | MPa | SO 527-1/-2 |
| Yield strain | 25 | % | ISO 527-1/-2 |
| Nominal strain at break | 45 | % | ISO 527-1/-2 |
| Flexural Modulus | 2850 | MPa | ISO 178 |
| Flexural Stress at 3.5% | 77 | MPa | ISO 178 |
| Poisson’s ratio | 0.35 | ISO 527-1/-2 | |
| Tensile creep modulus | ISO 899-1 | ||
| 1h | 2700 | MPa | |
| 1000h | 1500 | MPa | |
| Charpy impact strength | ISO 179/1eU | ||
| 73°F | N | kJ/m² | |
| -22°F | 400 | kJ/m² | |
| Charpy notched impact strength | SO 179/1eA | ||
| 73°F | 15 | kJ/m² | |
| -22°F | 14 | kJ/m² | |
| lzod notched impact strength | ISO 180/1A | ||
| 73°F | 14 | kJ/m² | |
| -40°F | 12 | kJ/m² | |
| Hardness,Rockwell,M-scale | 88 | SO 2039-2 | |
| Hardness,Rockwell,R-scale | 119 | SO 2039-2 | |
| Thermal properties | Value | Unit | Test Standard |
| Melting temperature,18°F/min | 178 | ℃ | ISO 11357-1/-3 |
| Temp.of deflection under load | ISO 75-1/-2 | ||
| 260 psi | 95 | ℃ | |
| 65 psi | 155 | ℃ | |
| Vicat softening temperature | ISO 306 | ||
| 90°F/h,11 lbf | 160 | ℃ | |
| 90°F,2 lbf | 175 | ℃ | |
| Coeff.of linear therm.expansion,parallel | 110 | E-6/K | SO 11359-1/-2 |
| Coeff.of linear therm.expansion | ISO 11359-1/-2 | ||
| normal | 110 | E-6/K | |
| Normal,-40-23°℃ | 100 | E-6/K | |
| Parallel,-40-23°℃ | 100 | E-6/K | |
100P加工参数：
| Hold pressure range | 90-110 | MPa | |||||
| Hold pressure time | 8 | s/mm | |||||
| Annealing time,optional | 30 | min/mm | |||||
| Annealing temperature | 160 | C | |||||
| Extrusion | Value | Unit | Test Standard | ||||
| Drying Temperature | 75-85 | C | |||||
| Drying Time,Dehumidified Dryer | 2-4 | h | |||||
| Processing Moisture Content | ≤0.2 | % | |||||
| Melt Temperature Optimum | 200 | C | |||||
| Melt Temperature Range | 195-205 | ℃ | |||||
| Characteristics | |||||||
| Processing | ·Injection Molding | ·Sheet Extrusion | |||||
| ·Proile Extrusion | ·Other Extrusion | ||||||
| Delivery form | ·Pellets | ||||||
| Additives | ·Lubricants | ·Release agent | |||||
| Regional Availability | ·North America | ·Asia Pacific | ·Near East/Africa | ||||
| ·Europe | ·South and Central America | ·Global | |||||
| Processing Texts Injection molding | |||||||
| Drying is recommended,but not necessary for newly opened packaging stored ina dry location. Follow the drying guidelines above in the following cases: | |||||||
| -If moisture is above the Processing Moisture Content recommendation, ·When a resin container is damaged, | |||||||
| ·When the material is not properly stored in a dry place at room temperature,or ·When packaging stays open for a significant time. | |||||||
（免责声明：本数据采集自网络，仅供学习交流，如有疑问请联系生产厂家，以厂家说法为准。本资料版权归属于原作者，如有侵权，请联系删除）
可提供的资料：
产品物性表（TDS-ISO）、COA（出厂检测报告）、加工参数
Email:info@plaspowers.com
www.plaspowers.com
sister corporation:Sunengtag
Wechat: sunengpv
评价
目前还没有评价